A283GR. C Q195 steel plate-good weldability and formability

A283GR. C Q195 steel plate-good weldability and formability

Due to its high strength and good plasticity, A283 steel plate exhibits excellent work hardening properties during cold forming. This means that after repeated cold working deformation, the steel plate can still maintain good strength and hardness, while its ductility and toughness have also been improved. In addition, due to its good welding performance, the plates are easy to weld into parts of various shapes and sizes, and the welding quality is stable and reliable. A283 steel plates are widely used in the manufacturing of various mechanical parts, such as bolts, nuts, pins and other standard parts as well as various non-standard mechanical parts. In addition, they are also used in the manufacture of building structural materials, such as steel bars, steel pipes, steel plates, etc..

sales1@fuchuanmetal.com

Message

A36 Q235B S235JR Steel Plate-Standard Selection of Building Bridge Foundation Structure

A514 steel plate-used for key bearing parts of construction machinery and mining equipment

Product details

Product Description

Product Name	A283/Q195 Cold Rolled Steel Plate
Production Process	Hot Rolling, Cold Rolling
Material Standards	AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc.
Width	100mm-3000mm
Length	1m-12m, or Customized Size
Thickness	0.1mm-400mm
Delivery Conditions	Rolling, Annealing, Quenching, Tempered Or Standard
Surface Process	Ordinary, Wire Drawing, Laminated Film

Chemical Composition

A283	C max.	Mnmax.	Pmax.	Smax.	Si (Greater1 inch, less than 1/2 inch)	Si (Greater1/2 inch)	Cumin.
Grade A	0.14	0.90	0.035	0.04	0.40	0.15-0.40	0.20
Grade B	0.17	0.90	0.035	0.04	0.40	0.15-0.40	0.20
Grade C	0.24	0.90	0.035	0.04	0.40	0.15-0.40	0.20
Grade D	0.27	0.90	0.035	0.04	0.40	0.15-0.40	0.20

Mechanical Properties

A283	Tensile Strength		Yield Strength min.		Elongation Rate 8 Inches	Elongation Rate 2 Inches
Grade A	45000-60000 psi	310-415 MPa	24000 psi	165 MPa	27% min.	30% min.
Grade B	50000-65000 psi	345-450 MPa	27000 psi	185 MPa	25% min.	28% min.
Grade C	55000-75000 psi	380-515 MPa	30000 psi	205 MPa	22% min.	25% min.
Grade D	60000-80000 psi	415-550 MPa	33000 psi	230 MPa	20% min.	23% min.

Physical Performance

Physical Performance	Metric	Imperial
Density	7.80 g/cc	0.282 lb/in³

Scope of Application

ASTM A283 steel plate is a kind of low carbon steel with high strength and good formability. It is easy to process and manufacture, and can be safely welded by various welding methods. ASTM A283 steel plate is a structural carbon steel plate used for low or medium tensile strength applications. ASTM A283 steel plate is used in the manufacture of riveted, bolted and welded structures for storage tanks and cryogenic control vessels, bridges and buildings, including prefabricated buildings, warehouses and industrial commercial structures.